C92300 / CDA 923 Leaded Tin Bronze Alloys
Specification :
| CDA | ASTM | Asarcon | SAE | AMS | Federal | Military | Other |
|---|---|---|---|---|---|---|---|
| C923 | B505 B505M B143-2B |
81 | 621 J461 J462 |
QQ-C-390, D3; QQ-B-1005, COMP 6 |
MIL-B-11553, COMP 6 |
Chemical Composition :
| Cu%1 | Pb% | Sn% | Zn% | Fe% | P%2 | Ni%3 | Al% | S% | Sb% | Si% | |
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Chemical Composition according to ASTM B505/B505M-18
1In determining Cu min., Cu may be calculated as Cu + Ni. 2For continuous castings, P shall be 1.5%, max. 3Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.3% min. Single values represent maximums.
|
|||||||||||
| 85.00- 89.00 |
0.30- 1.00 |
7.50- 9.00 |
2.50- 5.00 |
0.25 | 0.05 | 1.00 | 0.005 | 0.05 | 0.25 | 0.005 | |
Machinability :
| Copper Alloy UNS No. | Machinability Rating | Density (lb/in3 at 68° F) |
|---|---|---|
| C923 | 42 | 0.317 |
Mechanical Properties :
|
Mechanical Properties according to ASTM B505/B505M-18
|
|||||||||||
| Tensile Strength, min | Yield Strength, at .5% Extension Under Load, min | Elongation, in 2 in. or 50 mm min | Brinell Hardness (500 kg load) | Remarks | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | typical BHN | ||||||
| 40 | 276 | 19 | 131 | 16 | 70 | ||||||
Physical Properties :
|
Physical Properties provided by CDA
|
|||||||||||
| US Customary | Metric | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Melting Point – Liquidus | 1830° F | 999 °C | |||||||||
| Melting Point – Solidus | 1570° F | 854 °C | |||||||||
| Incipient Melting | 600° F | 315 °C | |||||||||
| Density | 0.317 lb/in3 at 68° F | 8.77 gm/cm3 at 20 °C | |||||||||
| Specific Gravity | 8.77 | 8.77 | |||||||||
| Electrical Conductivity | 12% IACS at 68° F | 0.07 MegaSiemens/cm at 20 °C | |||||||||
| Thermal Conductivity | 43.20 Btu/sq ft/ft hr/°F at 68 °F | 74.8 W/m at 20 °C | |||||||||
| Coefficient of Thermal Expansion 68-392 | 10 · 10-6 per °F (68-392° F) | 17.3 · 10-6 per °C (20-200 °C) | |||||||||
| Specific Heat Capacity | 0.09 Btu/lb/°F at 68° F | 377.1 J/kg at 293 °C | |||||||||
| Modulus of Elasticity in Tension | 14000 ksi | 96500 MPa | |||||||||
Fabrication Properties :
|
Fabrication Properties provided by CDA
|
|||||||||||
| Joining Technique | Suitability | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Soldering | Excellent | ||||||||||
| Brazing | Good | ||||||||||
| Oxyacetylene Welding | Not Recommended | ||||||||||
| Gas Shielded Arc Welding | Not Recommended | ||||||||||
| Coated Metal Arc Welding | Not Recommended | ||||||||||
Thermal Properties :
|
Thermal Properties provided by CDA
|
|||||||||||
| Treatment | Temp./Time – US | Temp./Time – SI | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Stress Temperature | 500 | 260 | |||||||||
| Solution Minimum | |||||||||||
| Solution Maximum | |||||||||||
| Solution Time | 0.0 | ||||||||||
| Solution Medium | |||||||||||
| Precipitation Value | |||||||||||
| Precipitation Time | |||||||||||
| Precipitation Medium | |||||||||||
| Annealing Minimum | |||||||||||
| Annealing Maximum | |||||||||||
| Annealing Time | |||||||||||
| Hot Works Minimum | |||||||||||
| Hot Works Maximum | |||||||||||