C95300 / CDA 953 Aluminum Bronze Alloys
Specification :
CDA | ASTM | Asarcon | SAE | AMS | Federal | Military | Other |
---|---|---|---|---|---|---|---|
C953 | B505 B505M |
68B J461 J462 |
QQ-C-390, G7; QQ-B-671, Class 2 |
MIL-B-16033, Class 2 | Aluminum Bronze 9B |
Chemical Composition :
Cu% | Fe% | Al% | |||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Chemical Composition according to ASTM B505/B505M-18
Note: Cu + Sum of Named Elements, 99.0% min. Single values, unless otherwise noted, represent maximums.
|
|||||||||||
86.00 min |
0.80- 1.50 |
9.00- 11.00 |
Machinability :
Copper Alloy UNS No. | Machinability Rating | Density (lb/in3 at 68 °F) |
---|---|---|
C953 | 55 | 0.272 |
Mechanical Properties :
Mechanical Properties according to ASTM B505/B505M-18
|
|||||||||||
Tensile Strength, min | Yield Strength, at .5% Extension Under Load, min | Elongation, in 2 in. or 50 mm min | Brinell Hardness (3000 kg load) | Remarks | |||||||
---|---|---|---|---|---|---|---|---|---|---|---|
ksi | MPa | ksi | MPa | % | typical BHN | ||||||
70 | 483 | 26 | 179 | 25 | 125 |
Physical Properties :
US Customary | Metric | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Physical Properties provided by CDA
*Field Strength 8 kA/m
|
|||||||||||
Melting Point – Liquidus | 1913 °F | 1045 °C | |||||||||
Melting Point – Solidus | 1904 °F | 1040 °C | |||||||||
Density | 0.272 lb/in3 at 68 °F | 7.53 gm/cm3 at 20 °C | |||||||||
Specific Gravity | 7.53 | 7.53 | |||||||||
Electrical Conductivity | 13% IACS at 68 °F | 0.075 MegaSiemens/cm at 20 °C | |||||||||
Thermal Conductivity | 36.3 Btu · ft/(hr · ft2·°F) at 68 °F | 62.8 W/m at 20 °C | |||||||||
Coefficient of Thermal Expansion 68-572 | 9 · 10-6 per °F (68-572 °F) | 15.5 · 10-6 per °C (20-200 °C) | |||||||||
Specific Heat Capacity | 0.09 Btu/lb/°F at 68 °F | 377.1 J/kg at 293 °C | |||||||||
Modulus of Elasticity in Tension | 16000 ksi | 110000 MPa | |||||||||
Magnetic Permeability* | 1.07 | 1.07 |
Fabrication Properties :
Fabrication Properties provided by CDA
|
|||||||||||
Joining Technique | Suitability | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Soldering | Good | ||||||||||
Brazing | Good | ||||||||||
Oxyacetylene Welding | Not Recommended | ||||||||||
Gas Shielded Arc Welding | Excellent | ||||||||||
Coated Metal Arc Welding | Good |
Thermal Properties :
Thermal Properties provided by CDA
|
|||||||||||
Treatment | Temp./Time – US | Temp./Time – SI | |||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Stress Relief | 600 | 316 | |||||||||
Solution Minimum | 1585 | 863 | |||||||||
Solution Maximum | 1635 | 891 | |||||||||
Solution Time | 1 | ||||||||||
Solution Medium | Water | ||||||||||
Precipitation Value | |||||||||||
Precipitation Time | |||||||||||
Precipitation Medium | |||||||||||
Annealing Minimum | 1150 | 622 | |||||||||
Annealing Maximum | 1225 | 663 | |||||||||
Annealing Time | 1 | ||||||||||
Hot Treatment Minimum | |||||||||||
Hot Treatment Maximum |